In this experimental study, the differences were investigated inmechanical properties by applying aging process to AA2024 Aluminum alloy powdermetal and fully dense materials at various process temperatures and durations. For this purpose, thespecimen prepared in dimensions of 10 * 10 * 55 mm were taken intosolutionizing process and then aged at 160 ° C, 190 ° C and 220 ° C for4,8,12,16,20 hours, respectively. Beside hardness measurements of agedspecimens, 3-point bending tests were performed. In addition, aged specimenswere examined by using SEM. As a result of the study, the mechanical properties of fully densematerials were better than those of powder metal samples. In addition, themechanical properties (hardness and bending strength) for fully dense andpowder metal materials have reached the highest values ​​at 220 ° C processingtemperature and 12 hours processing time.    Bu deneysel çalışmada AA2024 Alüminyumalaşımından üretilmiş toz metal ve tam yoğun malzemelere farklı işlemsıcaklıklarında ve sürelerinde yaşlandırma işlemi uygulanarak alaşımın mekaniközelliklerinde meydana gelen değişimler belirlenmeye çalışılmıştır. Bu amaçla10*10*55 mm boyutlarında hazırlanan numuneler solüsyona alınmış daha sonra 160 °C,190 °C ve 220°C sıcaklıklarda 4,8,12,16,20 saat sürelerde yaşlandırma işleminetabi tutulmuşlardır. Yaşlandırılan numunelerin sertlik ölçümlerinin yanında 3noktadan eğme deneyleri yapılmıştır. Ayrıca yaşlandırılan numunelerin SEM ileiçyapı incelemeleri yapılmıştır. Çalışma sonucunda tam yoğun malzemelerinmekanik özellikleri toz metal numunelere göre daha yüksek elde edilmiştir.Ayrıca tam yoğun ve toz metal malzemeler için mekanik özelliklerin (sertlik veeğme dayanımı) 220°C işlem sıcaklığında ve 12 saat işlem süresinde en yüksekdeğerler elde edildiği sonucuna ulaşılmıştır.