Hızlı Soğutma Sürecinde Dörtlü Zr48Cu36Ag8Al8 İri Hacimli Metalik Camının Atomik Yapısının Gelişimi

Show simple item record

dc.creator Çeltek, Murat; TRAKYA ÜNİVERSİTESİ
dc.creator ŞENGÜL, Sedat; TRAKYA ÜNİVERSİTESİ
dc.creator DÖMEKELİ, Ünal; TRAKYA ÜNİVERSİTESİ
dc.date 2019-12-25T00:00:00Z
dc.date.accessioned 2020-01-02T08:33:56Z
dc.date.available 2020-01-02T08:33:56Z
dc.identifier https://dergipark.org.tr/tr/pub/sdufenbed/issue/49749/566570
dc.identifier 10.19113/sdufenbed.566570
dc.identifier.uri http://acikerisim.sdu.edu.tr/xmlui/handle/123456789/49346
dc.description Çalışmamızda Zr48Cu36Al8Ag8dörtlü alaşımının atomik yapısı ve cam oluşturma süreci moleküler dinamiksimülasyon ile gömülü atom metodu kullanılarak araştırıldı. Cam geçiş sürecinive sıcaklığa bağlı atomik yapı gelişimini araştırmak için ortalamahacim-sıcaklık eğrisi, çiftler dağılım fonksiyonu (PDF) ve çift analiz metodukullanıldı. 300 K’de hesaplanan toplam PDF, g(r),daha önce rapor edilen deneysel g(r)ile iyi bir uyum sağlamaktadır. Öte yandan ortalama hacim-sıcaklık grafiğindenyararlanılarak belirlenen cam geçiş sıcaklığı da deneysel değerlerlebirbirlerine yakındır. Zr-Zr ve Cu-Cu çiftlerinin kısmi PDF'lerin piklerisıcaklık düşüşüne bağlı olarak normal bir artış eğilimi gösterirken, Al-Al veAg-Ag çiftleri ise çok yüksek pikler üreterek anormal bir davranışsergilemektedir. Bu davranışın nedeninin simülasyon hücresindeki Al ve Agatomlarının topaklanması olduğu görülmüştür. Sistemin mikro yapısıincelendiğinde ise kısa menzil düzenin göstergesi olan 1431, 1541 ve 1551 bağlıçiftlerinin bütün sıcaklıklarda baskın olduğu gözlenmiştir. Azalan sıcaklıklabirlikte özellikle ideal ikosahedral düzeni temsil eden 1551 bağlı çiftlerininoranının artması sistemin kısa menzil düzeninin gelişerek artmaya devamettiğini göstermektedir. 
dc.description In our study, atomic structure and glass formationprocess of Zr48Cu36Al8Ag8quaternary alloy was investigated by molecular dynamic simulation usingembedded atom method. The average volume-temperature curve, the pairdistribution function (PDF) and the pair analysis method were used toinvestigate the glass transition process and the atomic structure developmentdepending on the temperature. The total PDF, g(r), calculated at 300 K is ingood agreement with previously reported experimental g(r). On the other hand, theglass transition temperature determined by using the average volume-temperaturegraph is close to that achieved with experimental works. The peaks of the partialPDFs of the Zr-Zr and Cu-Cu pairs inhibit a normal upward trend due to thetemperature drop, whereas the peaks of the Al-Al and Ag-Ag pairs exhibit anabnormal behavior by producing very high peaks. The reason for thisbehavior was the aggregation of Al and Ag atoms in the simulation cell. Whenthe microstructure of the system was examined, it was observed that the 1431,1541 and 1551 bonded pairs which are indicative of the short range order weredominant in all temperatures. The increase in the fraction of the 1551 bondedpairs, which represent the ideal icosahedral order together with the decreasingtemperature, shows that the short range order of the system continues todevelop and increase.
dc.format application/pdf
dc.language tr
dc.publisher Süleyman Demirel University
dc.publisher Süleyman Demirel Üniversitesi
dc.relation https://dergipark.org.tr/tr/download/article-file/882378
dc.source Volume: 23, Issue: 3 954-962 en-US
dc.source 1308-6529
dc.subject İri hacimli metalik camlar,Moleküler dinamik simülasyon,Çiftler dağılım fonksiyonu,Topaklanma
dc.subject Bulk metallic glasses,Molecular dynamic simulation,Pair distribution function,Aggregation
dc.title Hızlı Soğutma Sürecinde Dörtlü Zr48Cu36Ag8Al8 İri Hacimli Metalik Camının Atomik Yapısının Gelişimi tr-TR
dc.title The Evolution of Atomic Structure of the Zr48Cu36Ag8Al8 Bulk Metallic Glass in the Rapid Cooling Process en-US
dc.type info:eu-repo/semantics/article


Files in this item

Files Size Format View

There are no files associated with this item.

This item appears in the following Collection(s)

Show simple item record

Search DSpace


Browse

My Account