© 2022 This is an open access article under the terms of the CC-BY 4.0, which permits unrestricted use, distribution, and reproduction in any medium, provided the original author and source are credited.In this study, conventional bitumen tests were performed on bituminous binder modified with Cocamide Diethanolamide chemical at different ratios. According to results of tests, the most suitable additive ratio has been determined as 5%. However, it was concluded that indirect tensile strength and resistance to moisture of samples prepared with bituminous binder modified with 5% Cocamide Diethanolamide has been adversely affected. It was desired to investigate that whether these properties could be strengthened by yarn waste fibers. Firstly, the effect of 0.1%, 0.2% and 0.3% yarn waste fibers on samples prepared with reference bituminous binder was investigated. Obtained results showed that both indirect tensile strength and resistance to moisture of samples containing 0.1% yarn waste fiber increased. Therefore, 0.1%, 0.2% and 0.3% yarn waste fibers were added to the aggregate mixture and mixing of them with bituminous binder modified with 5% Cocamide Diethanolamide was provided. According to obtained results, different ratios of yarn waste fibers added to aggregate mixture did not have a positive effect on moisture sensitivity. Tensile strength ratio values of samples containing bituminous binder modified with 5% Cocamide Diethanolamide and yarn waste fibers added to the aggregate mixture did not provide specification limit.