| dc.description |
In this study, we report the production of β˝-Al2O3 solid electrolyte by using Seydişehir α-Al2O3. Alumina has to be low grain-sized to ensure α-β phase transformation. Therefore, grain refining process was applied to high grain sized Seydişehir alumina by jetmill grinding. Seydişehir alumina was calcined at 1200 0C for 2 hours. After calcination, calcined Al2O3 and Na2CO3 were mixed during 2 hours in the mill. The samples were pressed and sintered to obtain β˝-Al2O3. β˝-Al2O3 was obtained after sintering at 1550°C for 1 hour. Due to the formation of β˝-Al2O3, it is observed that dielectric properties increased. |
|
| dc.format |
application/pdf |
|
| dc.publisher |
Süleyman Demirel University |
|
| dc.publisher |
Süleyman Demirel Üniversitesi |
|
| dc.relation |
http://dergipark.org.tr/download/article-file/408868 |
|
| dc.source |
Volume: 21, Issue: 3
816-819 |
en-US |
| dc.source |
1308-6529 |
|
| dc.subject |
α-Al2O3,Calcination; Sintering; β-Al2O3; Dielectric properties |
|
| dc.title |
Investigation of the Production of β-Al<sub>2</sub>O<sub>3</sub> Solid Electrolyte from Seydişehir α-Al<sub>2</sub>O<sub>3</sub> |