| dc.description |
Buçalışmanın amacı, iki farklı AA2014 toz grubundan (önalaşımlı, elementelformda) elde edilen numunelerin mekaniktest sonuçları, kırık yüzey analizi ve metalografik çalışmalarınıkarşılaştırarak, elementel tozun kullanımıyla elde edilen değerlerin tasarımmalzemesi olarak yeterli mekanik özelliklere sahip olup olmadığını belirlemeyeçalışmaktır. Ön alaşımlı (AA2014), elemental alüminyum ve bakır tozlarıkullanılarak klasik toz metalurjisi (TM) yöntemiyle numuneler üretilmiştir.AA2014 alaşımının içerdiği oran kadar, ticari saf Alüminyum tozuna bakıreklenmiş ve dökümde soğuk presleme yapılmıştır. Benzer koşullarda, önalaşımlanmış (AA2014) tozlar ve element tozlarından benzer bir bileşim eldeetmek için harmanlama ve karıştırma işlemleri gerçekleştirilmiştir. Sinterlemekoşulları olarak, üç farklı sıcaklık (600°C, 610°C, 620°C) kullanılmış vesinterleme süresi sabit tutulmuştur (30 dakika). Bu aşamada, alüminyummatriksinin katı çözeltiler oluşturmak için Bakır atomlarını çözmesi beklenir. Budurumun gerçekleşmesini incelemek için metalografik çalışmalar yapılmıştır.Sonuç olarak, alüminyum ve bakır tozu, uzun bir kalıp ömrü için alaşımlı AA2014yerine elemental olarak kullanılabilir. |
|
| dc.description |
The purpose of the work is by comparing the mechanical tests results,fracture surface analysis and metallographical studies of the samples obtainedfrom two different groups of powders (prealloyed, elementally formed AA2014),trying to determine whether the values obtained by the use of elemental powdercan have sufficient mechanical properties as design material. Samples wasproduced by using pre-alloyed (AA2014), elemental aluminum and copper powdersby classical powder metallurgy (PM) method. As the same proportion that AA2014alloy contains, copper was added elementally to the commercial pure Aluminumpowder and cold compressing were performed in the cast. In the similarconditions, blending and mixing operations were carried out to obtain similarcomposition from pre-alloyed(AA2014)powders and elemental powders. In the sintering conditions, three differenttemperatures (600˚C, 610˚C, 620˚C) were used and the sintering time kept constant(30 mins) . At this stage, it is expected that the aluminum matrix willdissolve Copper atoms to form solid solution. Metallographic studies carried out to examinethe realization of this aspect. As a result, aluminum and copper powders can be used in elemental forminstead of pre-alloyed AA2014 for a long die life. |
|
| dc.format |
application/pdf |
|
| dc.language |
en |
|
| dc.publisher |
Süleyman Demirel University |
|
| dc.publisher |
Süleyman Demirel Üniversitesi |
|
| dc.relation |
http://dergipark.org.tr/download/article-file/593079 |
|
| dc.source |
Volume: 6, Issue: 4
701-706 |
en-US |
| dc.source |
1308-6693 |
|
| dc.subject |
Toz Metalurjisi,Elemental Aluminyum Tozu,Ön-alaşımlı 2014,Sinterleme,Mekanik Özellikler |
|
| dc.subject |
Powder metallurgy,Elemental Aluminum powder,Pre-alloyed AA2014,Sintering,Microstructure |
|
| dc.title |
AA2014 VE ELEMENTEL Al VE Cu TOZLARI KULLANILARAK T/M PARÇA İMALATI ŞARTLARININ DENEYSEL ARAŞTIRILMASI |
en-US |
| dc.title |
EXPERIMENTAL INVESTIGATION OF P/M PARTS MANUFACTURING CONDITIONS USING AA2014 AND ELEMENTAL AL AND CU POWDERS |