Metallurgical Characterization and kinetics of borided 34CrNiMo6 steel

Show simple item record

dc.creator UÇAR, NAZIM
dc.creator yiğit, MEHMET
dc.creator ÇALIK, ADNAN
dc.date 2020-12-01T00:00:00Z
dc.date.accessioned 2021-12-03T11:15:15Z
dc.date.available 2021-12-03T11:15:15Z
dc.identifier 10e4e341-ee20-4625-8966-c63df8f3cc68
dc.identifier 10.2478/adms-2020-0021
dc.identifier https://avesis.sdu.edu.tr/publication/details/10e4e341-ee20-4625-8966-c63df8f3cc68/oai
dc.identifier.uri http://acikerisim.sdu.edu.tr/xmlui/handle/123456789/90002
dc.description Boriding of 34CrNiMo6 steel was performed in a solid medium consisting of Ekabor-II powders at 1123, 1173 and 1223 K for 2, 4 and 6 h. Morphological and kinetic examinations of the boride layers were carried out by optical microscopy, scanning electron microscopy (SEM) and X-ray diffraction (XRD). The thicknesses of the boride layers ranged from 22 +/- 2.3 to 145 +/- 4.1 depending on boriding temperature and time. The hardness of boride layer was about 1857 HV0.1 after boriding for 6 h at 1223 K, while the hardness of the substrate was only around 238 HV0.1. Growth rate constants were found to be between 1.2.10(-13) - 9.8.10(-13) m(2)/s depending on temperature. The activation energy for boron diffusion was estimated as 239.4 +/- 8.6 kJ mol(-1). This value was comparable to the activation energies reported for medium carbon steels in the literature.
dc.language eng
dc.rights info:eu-repo/semantics/closedAccess
dc.title Metallurgical Characterization and kinetics of borided 34CrNiMo6 steel
dc.type info:eu-repo/semantics/article

Files in this item

Files Size Format View

There are no files associated with this item.

This item appears in the following Collection(s)

Show simple item record

Search DSpace

Advanced Search


My Account