| dc.creator |
ALDEMİR, Durmuş Ali |
|
| dc.creator |
KALELİ, Murat |
|
| dc.creator |
Lapa, Havva Elif |
|
| dc.creator |
Şen, Esra |
|
| dc.date |
2024-10-20T00:00:00Z |
|
| dc.date.accessioned |
2025-02-25T10:18:35Z |
|
| dc.date.available |
2025-02-25T10:18:35Z |
|
| dc.identifier |
2459345e-af20-4c3e-9bd4-9d15cb4d5eea |
|
| dc.identifier |
10.1142/s0217984924502749 |
|
| dc.identifier |
https://avesis.sdu.edu.tr/publication/details/2459345e-af20-4c3e-9bd4-9d15cb4d5eea/oai |
|
| dc.identifier.uri |
http://acikerisim.sdu.edu.tr/xmlui/handle/123456789/99080 |
|
| dc.description |
All layers of MASnI2Br-based perovskite solar cells (PSCs) were deposited by ultrasonic spray pyrolysis method. The depositions of the layers were carried out in a large area. The perovskite thin ¯lm deposited on FTO/TiO2 had large grains. The crystallite size of the ¯lm was calculated as 90 nm from the XRD pattern. The bandgap of 1.54 eV was determined from the UV-visible measurement of MASnI2Br thin ¯lm. The PSCs with the di®erent active areas (0.3 cm2 and 3.18 cm2Þ were fabricated. The champion cells' power conversion e±ciencies were recorded at 0.181% and 0.120% for 0.3 cm2 and 3.18 cm2, respectively. |
|
| dc.language |
eng |
|
| dc.rights |
info:eu-repo/semantics/closedAccess |
|
| dc.title |
Scalable deposition of MASnI2Br-based perovskite solar cells via ultrasonic spray pyrolysis |
|