ZnOis one of the most widely used semiconductors for opto-electronic applicationsdue to its tunable band gap energy, high optical transparency in visible region. The effect of different monoethanolamine (MEA)ratio on structural, morphological and optical properties of ZnO thin films wasinvestigated in this study. A nano-fiber like structured ZnO was fabricatedthrough facile sol-gel dip coating process on glass substrates without anyfurther treatment. We observed that the peak intensity of samples increased andthe amount of defects in the crystal could be further decreased by rising its ofmonoethanolamine. Besides, the micro-fiber like grains of the ZnO covered theglass surface quite densely when the monoethanolamine content increased. Theoptical study showed that the transparency of the films could be enhanced byincreasing the amount of stabilizer.Çinko oksit yarıiletkenisahip olduğu değiştirilebilir yasak enerji aralığı ve görünür ışık bölgesindekiyüksek optik geçirgenliğinden dolayı opto-elektronik uygulamalar için çok sıkkullanılan yarıiletkenlerden biridir. Farklı miktarlarda kullanılan monoethanolaminmiktarının ZnO ince filmlerin yapısal, morfolojik ve optik özellikleri üzerineetkileri bu çalışmada incelenmiştir. Nano-fiber yapılı ZnO ince filmler başkaherhangi bir işlem gerektirmeden cam altlık üzerine, basit sol-jel daldırmayöntemi kullanılarak sentezlenmiştir. Monoetanolamin miktarı artırıldığındaörneklerin XRD pik şiddetlerinin arttığı ve kristal kusurlarının azaldığıgözlemlenmiştir. Bunun yanında, monoetanolamin miktarı arttığında mikro-fiberZnO taneciklerinin altlık yüzeyini oldukça yoğun bir şekilde kapladığıgörünmüştür. Ayrıca optik ölçümler sonucu stabilizer olarak kullanılan monoethanolaminmiktarının artışı ile ince filmlerin görünür ışık bölgesindeki geçirgenliğininarttığı görülmüştür.