Titanium alloys are usedin many specific applicants such as biomedical, military, sporting goods andaerospace industry due to their high strength properties and low aspect ratio.Even though their outstanding properties, titanium alloys have low utilizationrate and relatively low recycling ratio during manufacturing of Titanium parts.In order to determine its mechanical and impact properties for low-costTi-based alloy applications, powder size distribution and compacting pressurestrongly affect the microstructural properties of the sintered Ti-6Al-4V alloy.This paper presents how the narrow particle size distribution affect the impactproperties of both recycled and commercially available Ti-6Al-4V alloys. Below40µm particle size distribution range of Ti-6Al-4V alloys were conducted on3-point bending, Charpy impact test and microstructural evaluation. Resultsindicate that -40µm size distributed and recycled Ti-6Al-4V alloys show morebrittle behaviour than commercial available alloys.Titanyum alaşımları yüksek kütle – dayanım oranı gibiözellikleri sayesinde, biyomedikal, askeri, spor ve havacılık gibi birçokendüstriyel alanda kullanılmaktadır. Birçok endüstriyel alanda tercihedilmesine rağmen, yüksek maliyeti ve düşük geri dönüşüm oranı titanyum alaşımımalzemelerin kullanım alanlarını kısıtlamaktadır. Bu çalışma kapsamında partikülboyut dağılımının, ticari ve geri dönüştürülmüş toz metal Ti-6Al-4Valaşımlarının darbe dayanımları üzerindeki etkileri araştırılmayaçalışılmıştır. Bu kapsamda -40 µm toz partikül boyutundaki TM numunelere Charpydarbe testi uygulanmış ve numunelerin mikroyapıları incelenmiştir. Sonuçlar -40 µm toz partikül boyutundaki numuneleriçin ticari toz ile üretilenlerin daha yüksek dayanım değerlerine ulaştığıgöstermektedir.