Super alloys are widely used in the field of aviationand they are difficult to machine. Alumina and silicon nitride based ceramicmatrix composites have been used for super alloy machining. Since SiAlON basedceramic cutting tools can be produced with gas pressure sintering method whichis suitable for serial production, they provide cost advantages over Al2O3-SiCwcutting tools. However SiAlON ceramics have the disadvantage for super alloymachining due to inadequate properties in respect of chemical durability.Therefore in this study in order to enhance chemical durability of SiAlONceramics, SiAlON based ceramics prepared with unique compositional design withTiN incorporation. SiAlON-TiN composites were prepared in pilot scale whichallows description of the problems and their solutions. The optimization effortsin the production process of SiAlON-TiN cutting tools with the desiredproperties have been achieved in a pilot scale.    Süperalaşımlar havacılık alanında yaygın olarak kullanılan ve işlenmesizor malzemelerdir. Alümina ve silisyum nitrür esaslı seramik matrislikompozitler süperalaşımların işlenmesinde kullanılmaktadırlar. SiAlON esaslıseramik kesici uçlar seri üretime uygun gaz basınçlı sinterleme tekniği ileüretilebildikleri için Al2O3-SiCw kesiciuçlara karşı maliyet avantajı sağlamaktadırlar. Ancak SiAlON seramiklerikimyasal dayanım açısından süperalaşım işlenmesinde yeterli değildir. Bunedenle bu çalışmada SiAlON seramiklerinin kimyasal dayanımını arttırmak içinTiN ilavesi yapılarak özgün komposizyon tasarımlarıyla hazırlanmış SiAlON-TiNkompozitlerinin pilot ölçekte üretimi yapılarak, üretim esnasında karşılaşılansorunlar ve çözüm önerileri açıklanmıştır. Üretim sürecinde yapılanoptimizasyon çalışmaları neticesinde istenen özelliklerde kesici uç üretimipilot ölçekte başarılmıştır.