In this study, impact behaviors of glass fiber/epoxy composite plateshave been investigated, experimentally. For this purpose, composite samples have been manufactured in dimensionsof 100x100 mm and with layer of 8. The specimens kept into hydrochloric acid solutions(acid concentration 15% and 25%)   in aclosed glass jar in sunless for different exposure times at room temperature. Impact tests were performed using FractovisPlus impact test machine at two different impact energies (20J and 30J). Afterimpact tests, force- deflection curves, impact energy- deflection,velocity-time and force-time have been plotted. The experiments resultsobtained from the specimens kept into hydrochloric acid solutions werecompared with no immersed specimens. As a result of experimental studies, itwas seen the acidic environment reduced the load carrying capacity of compositespecimens but did not change the curve type. Bu çalışmada, cam elyaf takviyeli epoksi kompozitnumunelerin darbe davranışı deneysel olarak incelenmiştir. Bu amaçla 100x100 mmboyutlarında 8 tabakalı kompozit numuneler vakum infüzyon yöntemi kullanılaraküretilmiştir. Numuneler, oda sıcaklığında güneş görmeyen kapalı bir kavanozdakihidroklorik asit çözeltisi (asit derişikliği %15 ve % 25) içinde, farklısürelerde bekletilmiştir. Darbe testleri Fractovis Plus darbe test cihazıkullanılarak, iki farklı darbe enerjisinde (20J ve 30J) gerçekleştirilmiştir. Kuvvetçökme eğrileri, darbe enerjisi-maksimum kuvvet eğrileri, darbe enerjisi, çökmeeğrileri, hız-zaman eğrileri ve kuvvet-zaman eğrileri çizilmiştir. Hidroklorikasit çözeltisinde bekletilen numunelerden elde edilen deney sonuçları ile odasıcaklığında bekletilen numunelerden elde edilen sonuçlar karşılaştırılmıştır.Deneysel çalışma sonucunda, asidik ortamın kompozit numunelerin yük taşımakapasitesini azalttığı fakat eğri tipini değiştirmediği görülmüştür.