Inthis study, nano SiC particles with different ratios of 0.25, 0.5 and 1 wt%were added to the pure Al, and then the powder mixtures were subjected tomechanical alloying and sintering by hot press. After sintering process,samples were metallographically prepared for wear and bending tests. Theresults showed that the addition of a certain amount of nano SiC particlesincreased the wear resistance of pure Al matrix. The similar results wereobtained after bending test results. In order to study the distribution ofreinforcement particles in the structure, elemental distribution analysis wasperformed with EDX analysis. The results were evaluated in detail.
Buçalışmada saf alüminyum (Al) matris içerisine ağırlıkça % 0.25, 0.5 ve 1oranlarında nano silisyum karbür partikülleri ilave edilmiş ve ardından tozkarışımları önce mekanik alaşımlama, daha sonra sıcak pres ile sinterlemeişlemine tabi tutulmuştur. Sinterleme sonrasında elde edilen numunelermetalografik işlemler ile hazırlanıp aşınma ve eğilme testlerine tabitutulmuştur. Aşınma testleri sonucunda, saf Al matrise artan miktardananopartikül ilavesinin, belli orana kadar aşınma direncini arttırdığıgözlenmiştir. Benzer şekilde, artan nanopartikül takviyesiyle, eğilme testisonuçlarında da gözle görülür artışın olduğu gözlenmiştir. Takviyepartiküllerinin yapı içerisindeki dağılımını incelemek amacıyla numunelere EDXanalizi ile elementel dağılım analizi yapılmıştır. Elde edilen sonuçlarliteratür ile karşılaştırılarak değerlendirilmiştir.